D. He, F. Zhang, J. Jiang, B. Fu, X. Li, Beijing University of Technology, Beijing, China
Iron base composite coatings were deposited on mild steel substrate by arc spraying and cored wire with TiC ceramic powders. The abrasion wear resistance properties were examined on the MLS-225 wet sand/rubber wheel tester. The microstructure, phase compositions and worn surface morphologies of the coatings were observed by means of optical, scanning electron microscopy and X-ray diffraction .The results showed that composite coatings with TiC ceramic hard phases was reinforced by the TiC hard particles distributed in the iron-based coating. The average microhardness of the coatings is about 1137 HV0.1. The coatings have the excellent abrasive wear resistance which is 6 times higher than that of the Q235 mild steel. Wear mechanisms of coatings was mainly micro-ploughing and brittle fracture.