J. L. McDougall, M. E. Stevenson, Metals & Materials Engineers, Suwanee, GA
Specimens of copper tubing from an industrial scale chiller were subjected to a complete corrosion failure analysis. Non-destructive inspection of the tubing indicated substantial corrosion damage and provided the impetus for the corrosion analysis. By application of the typical methods encountered in metallurgical failure investigations, as well as additional chemical analysis techniques, the most probable cause of failure was identified to be a change in the water chemistry during the service life of the tubes. Additional items that may have contributed to the failure include the geometric design of the tube and the post-manufacture cleaning process prior to service. Recommendations were made regarding water treatment and the requirements for any replacement tubes. In addition to discussion of the specific failure(s) investigated, notes regarding the general procedures for corrosion failure analysis are also presented.
Summary: Copper tubing from an industrial chiller was subjected to a complete corrosion failure analysis. Inspection of the tubing indicated substantial corrosion. A metallurgical failure investigation coupled with additional chemical analysis allowed for the most probable cause of failure to be identified. Recommendations were made regarding water treatment.