10.4
Surface Treatment for 20nm SRAM Devices to Overcome Tip Curvature Radius Limitation in Conductive AFM Analysis
Surface Treatment for 20nm SRAM Devices to Overcome Tip Curvature Radius Limitation in Conductive AFM Analysis
Monday, November 4, 2013
The Tech Museum
Summary:
Conductive-Atomic Force Microscopy (C-AFM) is a popular failure analysis method used for localization of failures in Static Random Access Memory (SRAM) devices. The SRAM structure has a highly repetitive pattern where any abnormality in a failed cell compared to neighboring cells could be easily identified from its current image. Unlike topographical imaging, the C-AFM requires the probe tip to be coated with a conductive layer in order to pick up the electrical signals from the device under test. The coating needs to be sufficiently thick as it would wear off after a certain amount of physical scanning. This additional coating on the AFM tip is essential but poses a limit to the tip radius curvature. The commercially available tip radius is approximately 35nm (DDESP-10 from Bruker) and the dimension is too large for imaging of 20nm technology device. However, the limitation could be alleviated by subjecting the sample surface to treatment prior to C-AFM imaging. The aim of this surface treatment is to ensure C AFM tip maintains sufficient scanning contact with the tiny conductive (tungsten) structure of the sample in order to achieve distinct current image. The surface treatment is done by creating a receding Inter-Layer Dielectric (ILD) from its neighboring tungsten contact. The creation of the receding depth could be achieved by either wet etching or dry etching (Reactive Ion Etching, RIE). In this work, the surface treatments by these two methods have been investigated and the recipe is optimized to obtain a clear current image. The developed surface treatment method has been applied on three defective 20nm SRAM cells and the failed components have been successfully analyzed with the root cause identified.
Conductive-Atomic Force Microscopy (C-AFM) is a popular failure analysis method used for localization of failures in Static Random Access Memory (SRAM) devices. The SRAM structure has a highly repetitive pattern where any abnormality in a failed cell compared to neighboring cells could be easily identified from its current image. Unlike topographical imaging, the C-AFM requires the probe tip to be coated with a conductive layer in order to pick up the electrical signals from the device under test. The coating needs to be sufficiently thick as it would wear off after a certain amount of physical scanning. This additional coating on the AFM tip is essential but poses a limit to the tip radius curvature. The commercially available tip radius is approximately 35nm (DDESP-10 from Bruker) and the dimension is too large for imaging of 20nm technology device. However, the limitation could be alleviated by subjecting the sample surface to treatment prior to C-AFM imaging. The aim of this surface treatment is to ensure C AFM tip maintains sufficient scanning contact with the tiny conductive (tungsten) structure of the sample in order to achieve distinct current image. The surface treatment is done by creating a receding Inter-Layer Dielectric (ILD) from its neighboring tungsten contact. The creation of the receding depth could be achieved by either wet etching or dry etching (Reactive Ion Etching, RIE). In this work, the surface treatments by these two methods have been investigated and the recipe is optimized to obtain a clear current image. The developed surface treatment method has been applied on three defective 20nm SRAM cells and the failed components have been successfully analyzed with the root cause identified.